型号：LEXAN 103R Resin
品名：PC
厂家：SABIC Innovative Plastics
特性：无卤
用途：室外应用
加工方法：注射成型
物理性能额定值单位制测试方法比重
ASTM D792--1.20g/cm³ASTM D792--1.19g/cm³ASTM D792特定体积0.835cm³/gASTM D792熔流率（熔体流动速率）(300°C/1.2 kg)7.0g/10 minASTM D1238收缩率 - 流动(3.20 mm)0.50 到 0.70%内部方法吸水率
ASTM D57024 hr0.15%ASTM D570平衡, 23°C0.35%ASTM D570平衡, 100°C0.58%ASTM D570室外适用性f1
UL 746C硬度额定值单位制测试方法洛氏硬度
ASTM D785M 级70
ASTM D785R 级118
ASTM D785机械性能额定值单位制测试方法抗张强度1
ASTM D638屈服62.1MPaASTM D638断裂65.5MPaASTM D638伸长率2
ASTM D638屈服7.0%ASTM D638断裂110%ASTM D638弯曲模量3(50.0 mm 跨距)2340MPaASTM D790弯曲强度4(屈服, 50.0 mm 跨距)93.1MPaASTM D790泰伯耐磨性(1000 Cycles, 1000 g, CS-17 转轮)10.0mgASTM D1044冲击性能额定值单位制测试方法悬壁梁缺口冲击强度(23°C)910J/mASTM D256无缺口悬臂梁冲击(23°C)3200J/mASTM D4812落锤冲击(23°C)169JASTM D3029拉伸冲击强度5546kJ/m²ASTM D1822热性能额定值单位制测试方法载荷下热变形温度
ASTM D6480.45 MPa, 未退火, 6.40 mm138°CASTM D6481.8 MPa, 未退火, 6.40 mm132°CASTM D648维卡软化温度154°CASTM D15256线形热膨胀系数 - 流动(-40 到 95°C)6.8E-5cm/cm/°CASTM E831比热1260J/kg/°CASTM C351导热系数0.19W/m/KASTM C177RTI Elec130°CUL 746RTI Imp130°CUL 746RTI130°CUL 746电气性能额定值单位制测试方法体积电阻率> 1.0E+17ohms·cmASTM D257介电强度(3.20 mm, in Air)15kV/mmASTM D149介电常数
ASTM D15050 Hz3.17
ASTM D15060 Hz3.17
ASTM D1501 MHz2.96
ASTM D150耗散因数
ASTM D15050 Hz9.0E-4
ASTM D15060 Hz9.0E-4
ASTM D1501 MHz0.010
ASTM D150相比耐漏电起痕指数(CTI)PLC 2
UL 746高电弧燃烧指数(HAI)PLC 1
UL 746高电压电弧起痕速率 (HVTR)PLC 2
UL 746热丝引燃 (HWI)PLC 4
UL 746可燃性额定值单位制测试方法UL 阻燃等级(0.762 mm)HB
UL 94光学性能额定值单位制测试方法折射率1.586
ASTM D542透射率(2540 µm)88.0%ASTM D1003雾度(2540 µm)1.0%ASTM D1003注射额定值单位制
干燥温度121°C
干燥时间3.0 到 4.0hr
干燥时间，48hr
建议的水分含量0.020%
建议注射量40 到 60%
料筒后部温度288 到 310°C
料筒中部温度299 到 321°C
料筒前部温度310 到 332°C
射嘴温度304 到 327°C
加工（熔体）温度310 到 332°C
模具温度